%0 Conference Paper %A Rzyankina, Ekaterina %A M, Pytel, %A N, Mahomed, %A A., Nowotnik, %D 2019 %T Solution Heat Treatment of Single Crystal Castings of CMSX-4 Nickel-base Superalloy %U https://esango.cput.ac.za/articles/conference_contribution/Solution_Heat_Treatment_of_Single_Crystal_Castings_of_CMSX-4_Nickel-base_Superalloy/9114488 %R 10.25381/cput.9114488.v1 %K Nickel-base superalloys %K CMSX-4 %K single crystal castings %K solution heat treatment %K Aerospace Engineering %K Aerospace Materials %K Engineering Practice %K Machining %K Manufacturing Engineering not elsewhere classified %K Mechanical Engineering %K Materials Engineering not elsewhere classified %X
An investigation of the microstructure and mechanical properties for heat treated directionally cast rods, produced from the nickel-based superalloy, CMSX-4, is presented. The rods were cast using the Bridgman method for manufacturing single crystal structures. The microstructure of the cast rods consists of γ and γ' precipitates. This microsegregation has a negative effect on the microstructure and, hence, the mechanical properties of the castings. The solution heat treatment of the second generation, single crystal Ni-base superalloy, CMSX-4, is known to dissolve the eutectic γ and γ' region. This requires temperatures up to 1316°C and approximately 45 hours total time. These high temperatures and long processing times result in high costs. The aim of this study is to investigate the effect of the heat treatment protocol on the extent of improvement of
quality of single crystal castings, as a basis for determining cost feasibility in practice.
%I Cape Peninsula University of Technology